SHF 345

Standards

EN ISO 14174 S A CS 3
TS EN ISO 14174 S A CS 3

Properties and Applications

Alloyed and agglomerated flux, which is designed for submerged arc hardfacing of parts subjected to metal to metal friction wear, moderate impart and low stress mineral abrasion. Provides weld metal with 400-475 HB hardness, when used with SW 702 wire electrode. Possible to use in direct current. Hardness and transfer of alloying elements to the weld metal depens on welding parameters used. Gives very smooth and clean weld bead surfaces, slag removal is very easy and generally slag is self releasing.

Typical Applications : Hardfacing of pinchrolls, sinter crushers etc.
Shf 345 Sert Dolgu

Wear Resistance Types


Abrasion

Adhesion

Impact

Temperature

Corrosion
Low
Medium
High
Very High

Typical Applications

Shf 345 Model Tipik Uygulamalar Shf 345 Model Tipik Uygulamalar Shf 345 Model Tipik Uygulamalar Shf 345 Model Tipik Uygulamalar

Typical Chemical Values of Weld Metal

Welding WireType of AnalysisCSiMnCrMo
SW 702Weld Deposit0.250.701.703.250.40

Typical Mechanical Values of Weld Metal(%)

Test ConditionWelding WireHardness (HB)Hardness (HRc)
As weldedSW 702400 - 47543 - 49

Application Information

Welding Positions :
Shf 345 Kaynak Pozisyonu Shf 345 Kaynak Pozisyonu

Polarity:

Shf 345 Kutuplama DC(+)

Welding Parameters & Efficiency :

Packaging Information

Product CodeWeight Of The Box (kg)Boxes Per PackageWeight Of The PackagePackaging Type
408050AGM225.0125.6Kraft Bag

Storage & Re-Drying Information

>The total drying duration should not exceed 10 hours ( also for repeated drying).
>During transportation and storage, it should be ensured that the packaging is not damaged or torn.
>It has to be dried at 350°C for 2 hours.