Unalloyed wire electrode for GMA (MIG/MAG) welding of unalloyed steels by using CO2 or mixed gases, depending on thickness of the base metal. Characterized by a reduced slag formation and smooth welding deposit. Particularly suitable for welding of galvanized and pre-paint steels, welding unalloyed steels in pipe-lines, boilers and tank construction. Suitable also welding thin metal plates and repair welds. A thin and homogeneous copper coating increases electrical conducvitiy and protects the wire from using.
Unalloyed wire electrode for GMA (MIG/MAG) welding of general structural steels, pipe steels, and cast steels using CO2 or mixed shielding gases, depending on thickness of hte base metal. Generally used in steel construction, shipbuilding, machine, tank, boiler production, automotive industry. Preheating is required, depending on the plate thickness and carbon equivalent of the base metal. A thin and homogeneous copper coating increases electrical conductivity and protects the wire from rusting.
Unalloyed wire electrode for GMA (MIG/MAG) welding of general structural steels, pipes and cast steels by using CO2 or mixed shielding gases can be used depending on thickness of the base metal. Generally used in steel construction, machine, tank, boiler production. Preheating is required, depending on the plate thickness and carbon equivalent of the base metal. A thin and homogeneous copper coating increases electrical conductivity and protects the wire from rusting.
Non-copper coated and unalloyed GMA (MIG/MAG) wire electrode, especially produced for welding without spatter or very low level of spatter. Suitable for welding of general structural steels, boiler steels, pipe steels and cast steels. Due to it's special coating provides stable arc and no spatter especially with mixed shielding gases which can be used depending on the thickness. Generally preferred in robotic applications, due to it's high welding performance without spatter and cleaning needs. Also provides cost advantages in cleaning after welding, torch spare part consumptions like, contact tip, spiral, driving wheel, anti-spatter sprey. Due to these advantages preferably used in automotive, machine and steel furniture production.
Non-copper coated and unalloyed GMA (MIG/MAG) wire electrode, especially produced for welding without spatter or very low level of spatter. Suitable for welding of general structural steels, boiler steels, pipe steels and cast steels. Due to it's special coating provides stable arc and no spatter especially with mixed shielding gases which can be used depending on the thickness. Generally preferred in robotic applications due to it's high welding performance without spatter and cleaning needs. Also provides cost advantages in cleaning after welding, torch spare part consumptions like, contact tip, spiral, driving wheel, anti-spatter sprey. Due to these advantages preferably used in automotive, machine and steel furniture production.
Micro-alloyed wire electrode for GMA (MIG/MAG) welding of unalloyed and low-alloy steels. Characterized by a reduced slag formation and smooth welding deposit. Due to its Al and Ti micro-alloy content, particularly suitable for single pass welding of galvanized, pre-painted, rusty and dirty steels, welding low alloy steels in pipe-lines, boilers and tank production. Suitable also welding in thin metal plates and repair welds. CO2 or mixed shielding gases can be used depending on the thickness of the base metal. A thin and homogeneous copper coating increases electrical conductivity and protects the wires from rusting.
Low alloyed wire electrode for GMA (MIG/MAG) welding of steels, which are subjected to operating temperatures down to -60°C. Weld metal has high strength and high toughness. Suitable to use in petrochemical, chemical, oil/gas industries and off-shore platforms, especially welding of pipes, boilers, tanks and valves, pumps which are made of cast or forged steels.
Low-alloyed GMA (MIG/MAG) welding wire designed for welding of weathering steels (like COR-TEN) with high mechanical properties. Due to nickel and copper alloys, it provides higher corrosion resistance then carbon steels. Suitable for welding in steel construction manufacturing such as bridge, stadium and steel construction.
Low alloyed wire electrode for GMA (MIG/MAG) welding of fine grained and high strength steels with yield strength of up to 690 N/mm2. Weld metal exhibits good toughness properties down to -60°C. Especially used in high strength pipe-lines, earthmoving and mining equipments, trucks, mobile cranes, concrete pumps cranes and lift productions.
Low alloyed wire electrode for GMA (MIG/MAG) welding of fine grained and high strength steels with yield strength of up to 690 N/mm2. Weld metal exhibits good toughness properties down to -40°C. Especially used in high strength pipe-lines, earthmoving and mining equipments, trucks, mobile cranes, concrete pumps cranes and lift productions.