Welding Electrodes

AWS/ASME SFA - 5.1

E6013

EN ISO 2560 - A

E 38 0 RC 11

TS EN ISO 2560 - A

E 38 0 RC 11

Especially suitable for welding in sheets thinner then 5 mm, galvanized sheets and tubes, primer painted, painted and slightly rusty steels and in production of tanks and boilers, tube installations. Very easily operated in positional welding, including vertically-down. Good gap-bridging. Smooth arc, well suited for tack-welding due to its easy arc striking and re-striking properties. Possible to use equally well both with AC and DC. Welds are smooth, slightly concave and blending into base metal without undercutting. Slag is self-releasing. 

AWS/ASME SFA - 5.1

E6013

EN ISO 2560 - A

E 42 0 RR 12

TS EN ISO 2560 - A

E 42 0 RR 12

Suitable for joining and repair welding of light steel fabrications, iron works, wrought iron works, agricultural machines, boiler, chassis of vehicles. Used in all position except vertical-down. Particularly suited for the welding of horizontal fillets. Very smooth weld bead appearance, with easy arc striking and re-striking properties, quite and stable arc with fine-droplet metal transfer. Possible to use equally well both with AC and DC. Slag is completely self-releasing.

AWS/ASME SFA - 5.1

E7014

EN ISO 2560 - A

E 42 0 RR 12

TS EN ISO 2560 - A

E 42 0 RR 12

Preferably used in mild steel fabrication, sheet metal and ornamental iron works on poor fit up joints. Due to its iron powder addition in covering, particularly suited for the welding of horizontal fillets grooves with higher speed. Suitable for all position welding except vertical-down. High current carrying capacity, low spatter. Quite, stable arc characteristics with fine and fast droplet metal transfer. Very easy arc striking and re-striking. Very smooth welds blending into base metal without undercuts. Slag is completely self-releasing. Possible to use equally well both with AC and DC.

AWS/ASME SFA - 5.1

E6027

EN ISO 2560 - A

E 38 2 RA 73

TS EN ISO 2560 - A

E 38 2 RA 73

Acid-rutile coated, high efficiency electrode having a weld metal approx 165 %. Especially designed for welding fillets and narrow angle grooves. Produces complete root fusion and equal-leg fillet welds. Suitable for welding of galvanized, primer painted and slightly rusted components. Due to its low Silicon (Si) content, weld metal is also suited for subsequent galvanizing, enamaling and rubber cladding after welding. Provides very smooth welds without undercut. Slag is easily released, even from narrow angles. Welds are of X-ray quality.

AWS/ASME SFA - 5.1

E6013

EN ISO 2560 - A

E 38 A RR 12

TS EN ISO 2560 - A

E 38 A RR 12

Rutile type heavy coated electrode which is especially used in fabrication and repair welds of molten zinc bath made of Armco iron and very low carbon steels. Weld metal ensures high crack resistance against the effect of molten zinc. Possible to use equally well both with AC and DC.

AWS/ASME SFA - 5.1

E6013

EN ISO 2560 - A

E 38 2 RB 12

TS EN ISO 2560 - A

E 38 2 RB 12

Rutile-basic type coated electrode, particularly suitable for welding root passes and positional welding in fabrication of pipes, boilers and tanks. Also suitable for depositing backing-up beads in submerged arc welding. Owing to its low Si-content, weld metal is suited for subsequent galvanizing and enamelling.

AWS/ASME SFA - 5.1

E7016 H8

EN ISO 2560 - A

E 42 4 B 12 H10

TS EN ISO 2560 - A

E 42 4 B 12 H10

ГОСТ Р ИСО 2560 - A

E 42 4 B 12 H10

Multi-purpose electrode for assembly work, workshop and maintenance welding. Particularly used for repair welding of earthmoving equipment booms and approved for rail joint welding. Suitable for root passes as well as positional welding. Smooth and clean welds, merging into base metal without undercuts. Good gap bridging properties. Welds are of X-ray quality.

AWS/ASME SFA - 5.1

E7016 H8

EN ISO 2560 - A

E 42 3 B 12 H10

TS EN ISO 2560 - A

E 42 3 B 12 H10

Suitable for fabrication and repair welding of dynamically loaded steel constructions, machines and agricultural equipments, workshop and maintenence welding. Smooth and clean welds, blending into base metal without undercuts. Excellent gap bridging properties. The double covering of this electrode produces a stable, concentrated and directed arc, thus being ideally suited for root pass and positional welding and is suited for AC welding. Welds are of X-ray quality.

AWS/ASME SFA - 5.1

E7018 H8

EN ISO 2560 - A

E 42 3 B 42 H10

TS EN ISO 2560 - A

E 42 3 B 42 H10

Suitable for welding fabrication of dynamically loaded steel contructions, bridge, shipbuilding, pipe-line, pressure vessels, tanks, boiler and machines where high tougness is required. Weld metal recovery is appx. 115 %. Smooth and clean welds merging into base metal without undercuts. Good gap bridging properties. Welds are of X-ray quality. It is suited for depositing buffer layers on higher carbon steels.

AWS/ASME SFA - 5.1

E7018 H8

EN ISO 2560 - A

E 42 4 B 42 H5

TS EN ISO 2560 - A

E 42 4 B 42 H5

Suitable for welding fabrication of dynamically loaded heavy steel constructions, bridge, shipbuilding, pipe line, pressure vessels, tanks, boiler and machines where mechanical properties are required. Weld metal exhibits good toughness properties down to -50°C and produce tough and crack-free welded joints even on steels having a carbon content of up to 0.4%. Weld metal recovery amounts to approx. 120%. Welds are of X-ray quality. Electrode is suitable for depositing buffer layers on higher carbon steels.